Effect of the indentation process on fatigue life of drilled specimens
2015
Design and manufacture of mechanical elements are strongly influenced by the evaluation of the residual stresses due to their effects on the material strength. This paper presents numerical and experimental results performed on AW 6082-T6 aluminum alloy drilled specimens when the hole is created after a bilateral indentation process. The plastic deformation induced by the indenters creates a compressive residual stress field around the hole, which persists after the drilling operation. Several numerical analysis have been carried out in ANSYS APDL explicit solver for different indentation depths and hole diameters in order to evaluate the compressive circumferential stresses, optimal proces…
Effects of the indentation process on fatigue life of drilled specimens: optimization of the distance between adjacent holes
2016
The generation of permanent compressive stresses around the holes is recognized as a valuable mean to delay the onset and propagation of the defects and to extend the fatigue life of the mechanical components. In the work, a bilateral indentation process, performed on each side of the component, is widely used in order to create a residual circumferential stress field around the area to be drilled and that persists after the drilling operation. In order to evaluate the process parameters and to identify optimal geometric solutions, several static and fatigue tests are conducted on AW 6082-T6 aluminum alloy specimen where two holes are created. In particular, experimental tests on only drill…
Effect of Cold Working and Ring Indentation on Fatigue Life of Aluminum Alloy Specimens
2013
The article deals with the fatigue life of plates with hole made of aluminum alloy. Specifically, the combined effect of cold working expansion and ring indentation on improved fatigue life performance was investigated. Multiple fatigue tests were performed to determine the cycles to failure and the corresponding W¨ ohler diagram. Experimental results were compared with those of nontreated specimens. The conclusion was that cold working expansion and indentation create a delay on crack formation and fatigue failure.
Extracting work from random collisions: A model of a quantum heat engine
2022
We study the statistical distribution of the ergotropy and of the efficiency of a single-qubit battery ad of a single-qubit Otto engine, respectively fuelled by random collisions. The single qubit, our working fluid, is assumed to exchange energy with two reservoirs, a non-equilibrium "hot" reservoir and a zero temperature cold reservoir. The interactions between the qubit and the reservoirs is described in terms of a collision model of open system dynamics. The qubit interacts with the non-equilibrium reservoir (a large ensemble of qudits all prepared in the same pure state) via random unitary collisions and with the cold reservoir (a large ensemble of qubits in their ground state) via a p…
Effect of residual stresses and their redistribution on the fatigue crack growth in cold-worked holes
2009
The cold-expansion process is widely used to enhance the fatigue life of structures with fastener holes. Various studies assert that the cold-expansion improves the fatigue strength of fastener holes; however, the improvement of fatigue life is difficult to quantify. The influence on fatigue life of cold-worked hole in a 6061-T6 alluminum allosy was studied by numerical and experimental tests. Fatigue crack growth tests were carried out to find the crack length and growth rates of crack propagating from hole edge. Thus, the cold-expansion process was modeled with a Lagrangian implicit code for metal forming to obtain the residual stress field. Progressive crack growth along the observed fat…